S-3300

固体含量	91.0%
粘度 (Brookfield DVⅡ+,SC4-14/6R@25±1 ℃)	1 rpm –1,120 kcpsc 10 rpm –254 kcps 100 rpm –45 kcps

*Ref.

固体含量	90.0%
粘度 (Brookfield DVⅡ+, SC4-14/6R@25±1 ℃)	1 rpm –1,300 kcps 10 rpm –340 kcps 100 rpm –47 kcps

• Wafer type : Mono–Si (75Ω/□)

• 丝网

丝网

框架大小	网纱	EOM	Finger line opening
450 X450	400 mesh -18um stainless steel wire	19 um	60 um

• 印刷

印刷

刮刀速度	刮刀压力	间隙
200 ~ mm/s	0.1 MPa	1.0~2.0 mm

• 干燥 : 在红外干燥机温度为250~300℃下，20秒以内干燥

• 烘焙 :

Firing

温度(℃)	500	600	700
时间(秒)	6.8 ~ 8.4	4.6 ~ 5.8	2.1 ~ 4.0

Ag Paste for Solarcell S-3300

	Isc(A)	Voc(V)	Pm(W)	FF(%)	Eff(%)	Rer(Ω)	Rsh(Ω)
S-3300	8.870	0.639	4.578	80.78	19.16	0.00392	366
	8.878	0.638	4.567	80.64	19.11	0.00320	155
	8.906	0.640	4.616	80.97	19.32	0.00309	146
	8.862	0.638	4.581	80.99	19.17	0.00307	708
	8.872	0.638	4.598	81.17	19.24	0.00296	991
	8.855	0.637	4.555	80.73	19.06	0.00313	259
	8.866	0.638	4.576	80.86	19.15	0.00326	438
	8.895	0.639	4.594	80.88	19.23	0.00288	175
平均	8.875	0.638	4.583	80.88	19.18	0.00311	405

Ag Paste for Solarcell Ref

	Isc(A)	Voc(V)	Pm(W)	FF(%)	Eff(%)	Rer(Ω)	Rsh(Ω)
参考	8.877	0.637	4.614	81.61	19.31	0.00238	203
	8.816	0.637	4.552	81.02	19.05	0.00283	721
	8.812	0.638	4.555	80.98	19.06	0.00320	448
	8.805	0.638	4.567	81.34	19.11	0.00291	788
	8.814	0.636	4.557	81.28	19.07	0.00291	623
	8.807	0.638	4.552	81.00	19.05	0.00320	580
	8.829	0.639	4.567	80.99	19.11	0.00304	551
	8.807	0.638	4.550	80.96	19.04	0.00313	361
平均	8.821	0.638	4.564	81.15	19.10	0.00292	534