S-3300

Solid contents	91.0%
Viscosity (Brookfield DVⅡ+,SC4-14/6R@25±1 ℃)	1 rpm –1,120 kcpsc 10 rpm –254 kcps 100 rpm –45 kcps

S-3300

Solid contents	90.0%
Viscosity (Brookfield DVⅡ+, SC4-14/6R@25±1 ℃)	1 rpm –1,300 kcps 10 rpm –340 kcps 100 rpm –47 kcps

• Wafer type : Mono–Si (75Ω/□)

• Screen

Rework Screen

Frame Size	Mesh count	EOM	Finger line opening
450 X450	400 mesh -18um stainless steel wire	19 um	60 um

• Printing

Printing

Squeegee speed	Squeegee pressure	Off-contact distance
200 ~ mm/s	0.1 MPa	1.0~2.0 mm

• Drying : Dried in an IR dryer with set points 250~300℃ in less than 20 seconds

• Firing :

Firing

Temperature(℃)	500	600	700
Time(sec)	6.8 ~ 8.4	4.6 ~ 5.8	2.1 ~ 4.0

Ag Paste for Solarcell S-3300

	Isc(A)	Voc(V)	Pm(W)	FF(%)	Eff(%)	Rer(Ω)	Rsh(Ω)
S-3300	8.870	0.639	4.578	80.78	19.16	0.00392	366
	8.878	0.638	4.567	80.64	19.11	0.00320	155
	8.906	0.640	4.616	80.97	19.32	0.00309	146
	8.862	0.638	4.581	80.99	19.17	0.00307	708
	8.872	0.638	4.598	81.17	19.24	0.00296	991
	8.855	0.637	4.555	80.73	19.06	0.00313	259
	8.866	0.638	4.576	80.86	19.15	0.00326	438
	8.895	0.639	4.594	80.88	19.23	0.00288	175
Average	8.875	0.638	4.583	80.88	19.18	0.00311	405

Ag Paste for Solarcell Ref

	Isc(A)	Voc(V)	Pm(W)	FF(%)	Eff(%)	Rer(Ω)	Rsh(Ω)
Ref.	8.877	0.637	4.614	81.61	19.31	0.00238	203
	8.816	0.637	4.552	81.02	19.05	0.00283	721
	8.812	0.638	4.555	80.98	19.06	0.00320	448
	8.805	0.638	4.567	81.34	19.11	0.00291	788
	8.814	0.636	4.557	81.28	19.07	0.00291	623
	8.807	0.638	4.552	81.00	19.05	0.00320	580
	8.829	0.639	4.567	80.99	19.11	0.00304	551
	8.807	0.638	4.550	80.96	19.04	0.00313	361
Average	8.821	0.638	4.564	81.15	19.10	0.00292	534