Home > Ag-Paste > EO-S 0820L
| Model | S-0820L(A) | S-0820L(B) |
|---|---|---|
| Non-volatile Contents(wt%) | 79.0 | 79.0 |
| Viscosity(dpa*s) | 300±50 | 300±50 |
| Sheet Resistance(mΩ/□) | 120 | 100 |
| specific resistance(Ω*cm) | < 8.0X10-5 | < 6.5X10-5 |
| Thickness(um) | 5~6 | 5~6 |
| Adhesion(%) | 100 | 100 |
- Test Substrate : NITTO DENKO ERECRYSTA V270L-TFMD5 Film
- Printing Mesh : S/T500mesh, Wire diameter 18um, Emulsion thickness 10um
- Dry condition : 130℃X30min (Box Oven)
- Viscosity : Rion VT-04F, spindle #2 at 25℃
- Adhesion : Taping after Line Etching (3M #610)
- Laser Condition : IR Laser , Wavelength 1064nm
Pulse width 10~15
Pulse rate 200kHz Power 2.5~6W
Beam size < 40um
Mark Speed 400~1000mm/s